Rheology
Maryam Shokrollahi; Bahereh T. Marouf; Reza Bagheri
Abstract
Dimethylbenzylidene sorbitol (DMDBS) is a common nucleating/clarifier agent used in polypropylene (PP). So many researchers have looked at different aspects of incorporating this additive on crystallization behavior of PP. The current study has focused on a rather new subject and that is the role of ...
Read More
Dimethylbenzylidene sorbitol (DMDBS) is a common nucleating/clarifier agent used in polypropylene (PP). So many researchers have looked at different aspects of incorporating this additive on crystallization behavior of PP. The current study has focused on a rather new subject and that is the role of carrier resin of DMDBS masterbatch on the rheological behaviour of polypropylene. This goal has been achieved through studying the role of carrier resin on phase separation behavior of DMDBS upon cooling. It has been shown that a permanent bonding forms between the molecules of carrier resin and DMDBS in the masterbatch and this bonding slows down the crystallization kinetics of DMDBS in the final blend which in turn, influences its rheological behavior. Frequency sweep experiments conducted on a block co-polypropylene showed that lower values of storage shear modulus (G’), loss shear modulus (G’’), and complex shear viscosity (ɳ*) are observed if DMDBS is incorporated in the form of masterbatch. Interestingly, a different effect was observed when the masterbatch constituents were employed directly into the polypropylene, illustrating the importance of the mentioned bonding between DMDBS and the carrier resin in the masterbatch.
Characterization
Tao Zheng; Qian Li; Qian Zhou; Huayi Li; Qian Xing; Liaoyun Zhang; Youliang Hu
Abstract
9,10-Dihydro-9,10-ethano-anthracene-11,12-dicarboxylic acid disodium salt (DHEAS) was synthesized and used as a nucleating agent for poly(1-butene) (iPB). The isothermal crystallization kinetics of iPB having different nucleating agents were investigated by differential scanning calorimetry (DSC) and ...
Read More
9,10-Dihydro-9,10-ethano-anthracene-11,12-dicarboxylic acid disodium salt (DHEAS) was synthesized and used as a nucleating agent for poly(1-butene) (iPB). The isothermal crystallization kinetics of iPB having different nucleating agents were investigated by differential scanning calorimetry (DSC) and polarized optical microscopy (POM). The results showed that the nucleating agents increased the crystallization temperature and the crystallization rate and shortened the crystallization half-time (t1/2). As well, the nucleating agents could be used as heterogeneous nuclei in the iPB matrix and decreased the size of iPB. When the nucleating agent was DHEAS, the crystallization temperature of iPB was up to 93.6°C which was higher than that of other nucleating agents for iPB and pure iPB. The crystallization half-time in the presence of DHEAS was 0.58 min which was less than that of other nucleating agents for iPB and pure iPB. In this case, the spherulitic size of iPB was the smallest and the morphology was changed, which indicated that DHEAS displayed better nucleation effect among the studied nucleating agents.