Nina V. Semikolenova; Valentina N. Panchenko; Mikhail A. Matsko; Vladimir A. Zakharov
Abstract
For preparation of highly active supported catalyst with bis(imino)pyridyl Fe(II) complexes (Fe1, Fe2) and N,N-α-diimine complex of Ni (Ni3), silica modified with alumina (SiO2 (Al)) was used as a support. Data on the possibility to regulate molecular weight (MW) and molecular weight distribution ...
Read More
For preparation of highly active supported catalyst with bis(imino)pyridyl Fe(II) complexes (Fe1, Fe2) and N,N-α-diimine complex of Ni (Ni3), silica modified with alumina (SiO2 (Al)) was used as a support. Data on the possibility to regulate molecular weight (MW) and molecular weight distribution (MWD) of polyethylene (PE), produced over the supported catalyst Fe1/SiO2 (Al)+TIBA by variation of polymerization temperature and the addition of hydrogen and hexene-1, are obtained. The prepared PE samples were characterized by Mw values varied from 80 to 350 kg/mol and various MMD (Mw/Mn=4.6-11.7).By grafting on SiO2(Al) of two different iron bis(imino)pyridyl complexes, producing PE with diverse MW, bi-component catalyst was prepared. This catalyst generates linear PE with broad and bimodal MWD (Mw/Mn=33). Fixation on SiO2(Al) of α-diimine Ni(II) pre-catalyst (Ni3), yielding high molecular weight branched PE at the ethylene homopolymerization, and bis(imino)pyridyl Fe(II) complex (Fe2) that forms lower molecular weight linear PE, affords formation of a new bi-component catalyst. The catalyst produces PE with broad MWD and high content of branches concentrated in high molecular weight PE fraction.
Catalysis
Valentina Nikolaevna Panchenko; Ludmila Viktorovna Vorontsova; Vladimir Aleksandrovich Zakharov
Abstract
The interaction of the external donor (propyltrimethoxysilane - PTMS) with titanium-magnesium catalysts (TMCs) containing dibutylphthalate (DBP) as internal donor, which were prepared in different ways, was studied by chemical analysis and infrared diffuse reflectance spectroscopy (DRIFTS). The chemical ...
Read More
The interaction of the external donor (propyltrimethoxysilane - PTMS) with titanium-magnesium catalysts (TMCs) containing dibutylphthalate (DBP) as internal donor, which were prepared in different ways, was studied by chemical analysis and infrared diffuse reflectance spectroscopy (DRIFTS). The chemical composition of the catalysts after their interaction with heptane solutions of PTMS, PTMS/AlEt3 or AlEt3 during 1h at 70°C showed that this interaction led to removal of both TiCl4 and DBP from the catalysts. The fractions of DBP and Ti extracted, as well as the amounts of PTMS and AlEt3 bound, depended on the method of synthesizing the catalysts. DRIFT spectroscopy data concerning the state of DBP in the catalysts, before and after treatment with heptane solutions of PTMS or PTMS/AlEt3 during 1h at 70°C, showed that PTMS could substitute both TiCl4 and DBP, while adsorbing on coordinatively unsaturated Ti and Mg ions in the catalyst. The presence of AlEt3 played a key role in the interaction of PTMS with the catalyst. Activity data for propylene polymerization showed that treatment of TMC catalysts with PTMS before polymerization led to a sharp activity decrease due to deactivation of active sites, while the interaction of the catalyst with PTMS in the presence of AlEt3 led only to a slight decrease of activity, probably due to deactivation of non-stereospecific active centers.