Methanol dehydration is a high potential route for the production of light olefins (C2-C4). In this study, hierarchical Si-rich [B]-ZSM-5 catalysts (Si/Al= 200) were prepared through one-pot hydrothermal synthesis, including boron as a promoter and ethanol as a low-cost secondary template. N2 adsorptiondesorption, ...
Read More
Methanol dehydration is a high potential route for the production of light olefins (C2-C4). In this study, hierarchical Si-rich [B]-ZSM-5 catalysts (Si/Al= 200) were prepared through one-pot hydrothermal synthesis, including boron as a promoter and ethanol as a low-cost secondary template. N2 adsorptiondesorption, XRD, FE-SEM, and FT-IR techniques were applied to characterize the catalysts. The effect of different amounts of ethanol and different operating conditions was studied on the ZSM-5 catalyst preparation and performance in methanol-to-olefins (MTO) reaction. The results showed that the optimum amount of ethanol (ethanol/TPABr=5) led to the highest crystallinity (91.2%), the highest specific surface area (>400 m2g-1), and total pore volume (0.19 cm3g-1). The best catalytic performance was obtained at temperature of 480°C and methanol hourly space velocity (WHSV) of 7.2 h-1. The optimum catalyst had the highest propylene selectivity (58%) and light olefin selectivity (85%). The results proved the high capability of the new strategy for the efficient and fast development of the MTO catalyst.
Olefin oligomerization
Mohammad Rostamizadeh; Fereydoon Yaripour; Hossein Hazrati
Abstract
Highly siliceous ZSM-5 nanocatalysts can dehydrate methanol to a wide range of hydrocarbons. In this study, the development of hierarchical H-ZSM-5 nanocatalysts (Si/Al=200) were reported for the methanol-toolefins (MTO) reaction. The nanocatalysts were prepared through a hydrothermal technique and treated ...
Read More
Highly siliceous ZSM-5 nanocatalysts can dehydrate methanol to a wide range of hydrocarbons. In this study, the development of hierarchical H-ZSM-5 nanocatalysts (Si/Al=200) were reported for the methanol-toolefins (MTO) reaction. The nanocatalysts were prepared through a hydrothermal technique and treated by NaOH desilication. The parent and desilicated nanocatalysts were characterized using FE-SEM, XRD, FTIR, NH3-TPD and N2 adsorption-desorption techniques. The mesoporosity increased five times without significant collapse of the crystalline framework as a result of the appropriate desilication of H-ZSM-5 nanocatalyst. For the nanocatalyst, a high surface area of 189.5 m2 g-1, mesopore volume of 0.35 cm3 g-1 and well-adjusted strong acidity of 0.16 mmol NH3 g-1 resulted in a high methanol conversion of 100%, high propylene selectivity of 43% and low light paraffins selectivity of <8% in the MTO reaction. A broad mesopore size of 2-10 nm suppressed coke deposition and provided a long catalytic life time of 75 h. The developed high silica nanocatalyst showed a high potential for industrial applications due to its stable performance.